Fluoroadditive CPH200S is a white PTFE powder specialized for use as an additive to impart low surface energy and other fluoropolymer attributes. CPH200S is well suited for add in inks and coatings where a narrow particle size distribution is desired. It could improve lubricity and wear resistance when with plastics and rubbers.

Added to lubricants, it can enhance performance under severe conditions.CPH200S can be used at temperature from -190℃ to 250℃(-310℉ to 480℉).

CPH200S is generally designed to used as an additive, although it can also be used alone as a dry lubricants. It is unsuitable to be used as a molding or extrusion resin to replace for any of the high molecular weight PTFE resin.

CPH200S is inert to all chemicals and solvent. It is a good electrical insulator, does not absorb water, and is highly resistant to weathering.

Application
CPH200S is used as an additive in printing inks to improve certain properties, such as rub resistance, slip, surface smoothness and gloss. It can also reduce the "blocking". Typically,CPH200S is used in combination with polyethylene waxes to get the property modification. Due to its small particle size and narrow particle size distribution, CPH200S can be use in a variety of coating system to improve nonstick, antifriction, corrosion inhibition properties. It can also reduce the friction coefficient and increase the rub resistance.

Plastics and elastomers containing CPH200S have shown improved lubricity and reduced friction and wear. Typical loadings of 5-20% by weight were used.

Specification

Property	Test Method	Unit	Specification	Typical Value
Average Bulk Density	ASTM D4895	g/l	400-800	600
Melting Peak Temperature	ASTM D4894	℃	325±5	325±5
Average Particle Size	Laser Diffraction	μm	2-6	D10＜1 D50=4 D90＜9
Specific Surface Area	ASTM D4567	m2/g	0.8-4.5	1.5-3
Color	Enterprise standard	-	Bit Yellow	Bit Yellow

Packing
Packed in 25Kg plastic drum. Eight drums are packed on one pallet for easy shipping, handling and storage.

Safety Precaution
Before using CPH200S please read the Material Safety Data Sheet (MSDS) carefully.
Open and use containers only in well-ventilated areas using local exhaust ventilation. Vapor and fumes liberated during hot processing, or from smoking tobacco or cigarettes contaminated with CPH200S, may cause flu-like symptoms (chill, fever, sore throat). Vapor and fumes liberated during hot processing should be exhausted completely from work area. Contamination of tobacco with CPH200S should be avoided.

Mixtures with some finely divided metals, such as magnesium or aluminum, can be flammable or explosive under some conditions.